【摘 要】以煅燒法處理電解二氧化錳（EMD）工業礦渣原料，用工業水玻璃對其進行堿激發反應制備地聚物礦物膠凝材料。以抗壓強度為性能指標，單因素實驗考察了錳礦渣的煅燒溫度、水玻璃模數、液固比等條件對錳礦渣的堿激發反應活性的影響。

【關鍵詞】錳礦渣；煅燒；水玻璃；激發；抗壓強度

中圖分類號： X757；TU522.1 文獻標識碼： A 文章編號： 2095-2457（2018）04-0038-002

Study on Geopolymer Activity of Electrolytic Manganese Dioxide （EMD） Industrial Slag

ZHOU Shu-nian HUANG Lian-jin WANG Qiang

（Guangxi Normal University for Nationalities，Chongzuo Guangxi 532200，China）

【Abstract】The raw materials of electrolyzed manganese dioxide（EMD） industrial slag were treated by the calcination method，and alkali cementation reaction was conducted with industrial water glass to prepare geopolymeric mineral cementitious materials.Taking the compressive strength as the performance index，the single factor experiment investigated the influence of the calcination temperature of manganese slag，the modulus of the water glass， and the liquid-solid ratio on the alkali-activated reactivity of manganese slag.

【Key words】Manganese slag；Calcination；Water glass；Excitation；Compressive strength

礦渣的綜合利用是冶金工業共同面對的長期難題，錳礦加工工業中產生的廢棄渣含一定量的Al2O3、SiO2，經適當處理后可作為制備地聚物材料的前驅體原料，近年已有學者對此進行探索。如Wang Yong 等[1]將生石灰、石膏、水泥、錳尾礦渣和鋁粉按配比混合，制成了一種性能符合國家標準的混凝土；Hu Chunyan 等[2]用錳尾礦渣代替部分粘土并配以廢玻璃和高嶺土制成陶瓷磚。本文以廣西崇左市康密勞錳礦加工企業封存的原礦渣為原料，在不做摻入處理的情況下對其地聚物活性進行了研究。

1 材料與方法

1.1 材料與儀器

錳礦渣：取自廣西崇左市廣西埃赫曼康密勞化工有限公司儲存的桶裝原渣（主要生產電解二氧化錳和其他錳化工產品），600或700℃煅燒2h[3]，粉碎備用；液態工業水玻璃：購自廣西崇左市化工產品店，南寧化工股份有限公司生產，模數為3.1，Na2O含量為9.2%、SiO2含量為28.6%；氫氧化鈉（A.R）：成都市科龍化工試劑廠生產，用于調低水玻璃模數；去離子水：取自實驗室。

馬弗爐：101BS-2型，上海雙彪儀器設備有限公司；電子天平：BS-210g型，上海友聲衡器有限公司；電液式（數顯）萬能試驗機： WES-300D型，濟南品德試驗機有限公司；……