硫化鉬鎳礦加堿焙燒后鉬鎳的回收率分析

劉 美

（遼寧石油化工大學 石油化工學院，遼寧 撫順 113001）

硫化鉬鎳礦加堿焙燒后鉬鎳的回收率分析

劉 美

（遼寧石油化工大學 石油化工學院，遼寧 撫順 113001）

通過焙燒、水浸實現了原生硫化鎳鉬礦中鎳和鉬的分離，得到的較優工藝條件為：焙燒時，原礦和無水碳酸鈉質量比1∶0.9、560℃焙燒6h，650℃焙燒1.5h，焙砂中鎳品位為2.67%，鉬品位為5.81%；在固液比1∶4，溫度95℃的條件下，水浸焙燒渣2h，98.21%的鎳留在濾渣中，95.43%的鉬進入濾液，有效地實現了鉬和鎳的分離。

硫化鉬鎳礦;加堿焙燒;鉬鎳分離

Abstract:The Mo and Ni were separated from Mo-Ni sulfide ores by calcination and leach.The results of experiments showed that the tenor of nickel and molybdenum was 2.67%and 5.81%respectively during the calcination process with the mass ratio of raw ore to sodium carbonate was 1∶0.9,and the calcinations time was 6h at 560℃ and 1.5h at 650℃.Under the conditions of the solid-to-liquid ratio was 1∶4 and the leaching temperature was 95℃,after 2h immersion of calcinations slag,98.21%of nickel was remained in the filter slag and 95.43%of molybdenum was transferred into the filter liquor,and this achieved an efficient separation of Mo and Ni.

Key word:Mo-Ni sulfide ores;alkaline calcination;Mo-Ni separation

前 言

礦產資源是不可再生的一次性資源。我國礦產資源人均占有量遠低于世界平均水平，且礦產資源綜合利用率低，總回收率不到30%，因此，積極推進礦產資源和工業廢物的回收和綜合利用，是建設節約型社會和發展循環經濟的重要環節[1～2]。鉬鎳礦為我國獨有的多金屬復雜礦種，主要分布在湘、鄂、渝、黔、川、桂、陜、甘等省區[3]。由于該類礦石碳含量高，其鉬含量約為2.5%～6%，鉬主要以碳硫鉬礦存在于碳質頁巖中，且嵌布粒度極細[4～6]，因此采用常規選礦方法難以富集回收。

本次實驗對原生硫化鎳鉬礦采取碳酸鈉焙燒+水浸實現鎳鉬分離，獲得較好的回收效果。

1 實驗部分

1.1 試劑

無水碳酸鈉、氨水、硫酸、氟化鈉、鹽酸、檸檬酸銨、丁二酮肟、硝酸、紫脲酸銨、酚酞、氧化鋅、氯化鈉、硫酸、硫酸銅、硫酸氰鉀、硫脲、鉬酸鈉、乙二胺四乙酸二鈉均為分析純；硝酸，優級純。

1.2 礦樣的來源與性質

礦樣取自慈利某硫化鎳鉬礦，礦樣的大致組成及其含量如表1所示。……