硫硅酸鈣-硫鋁酸鹽水泥研究進展

蘇敦磊，董豐源，劉洪星，李秋義

(1.山東交通學院交通土建工程學院，濟南 250357；2.青島農業大學建筑工程學院，青島 266109)

0 引 言

圖1礦物的宏觀與微觀形貌[17,21-24]Fig.1 Macro and micro morphology of mineral[17,21-24]

圖2礦物兩次煅燒工藝制度[21]Fig.2 Process system of twice calcination of

圖3礦物穩定性與SO2和O2分壓、溫度的關系[24]Fig.3 Relationship between mineral stability and partial pressure of SO2 and O2， temperature[24]

圖5礦物的凈漿抗壓強度[21]Fig.5 Compressive strength of mineral paste[21]

圖6礦物水化產物的判定[21]Fig.6 Determination of hydration products of mineral[21]

圖7 鋁膠環境下和β-C2S的水化放熱曲線(%，質量分數)[29]Fig.7 Hydration heat release curves of and β-C2S in AH3 environment (%, mass fraction)[29]

表1 含鋁礦物體系水化產物的定量分析[30]Table 1 Quantitative analysis of hydration products of blended system[30]

(1)

(2)

(3)

(4)

(5)

(6)

2 TSAC的制備和性能

表2 TSAC制備和性能研究Table 2 Study on preparation and properties of TSAC

2.1 TSAC的制備

表3 和三種礦物的組成成分和形成晗Table 3 Component content and formation enthalpy of three minerals of β-C2S and

2.2 TSAC的性能

3 結語與展望

(1)固廢制備TSAC的研究較少，固廢基TSAC的水化理論研究不足，應深入挖掘具有鮮明特色的固廢原料或利用多種固廢原料協同制備TSAC，在實現水泥高性能化發展的同時兼顧固廢的資源化利用。

(2)TSAC凝結較快，調凝劑對該種新型水泥的作用效果和作用機制尚不明確，不僅要對現有常用調凝劑的影響展開系統研究，還應積極開發適用于TSAC的專用新型調凝組分。