鎳基合金ENiCrMo-10焊條的研制

陳燕 張學剛 陳波 陳佩寅 王猛

摘要： 鑒于目前工程上基本依賴進口ENiCrMo-10焊材的現狀，開展了ENiCrMo-10焊條的國產化研究。結果表明，通過調整藥皮中大理石、氟化物及硅酸鹽的比例，添加約20%的金屬粉，優化熔渣流動性，控制焊縫中S，P，B，Mo，Cr，W等元素的含量，研制的ENiCrMo-10焊條具有優良的平、立焊工藝性，較出色的耐晶間腐蝕、耐點腐蝕及抗裂性能，能夠滿足工程應用的技術要求。

關鍵詞： 鎳基合金焊條; 耐點腐蝕; 抗裂性能; 耐晶間腐蝕性能

中圖分類號： TG 422

Abstract： In view of the current situation that the project basically relies on imported ENiCrMo-10 welding materials， the research on the localization of ENiCrMo-10 electrode has been carried out. The results show that by adjusting the proportion of marble， fluoride and silicate in the coating， adding about 20% metal powder， optimizing the fluidity of slag， controlling the content of S， P， B， Mo， Cr， W and other elements in the weld， the ENiCrMo-10 electrode has excellent flat and vertical welding technology， excellent Intergranular corrosion resistance， pitting corrosion resistance and crack resistance， which can meet the requirements of engineering application.

Key words： nickel base alloy covered electrode; pitting corrosion resistance; crack resistance; intergranular corrosion resistance

0 前言

ENiCrMo-10焊條可用于哈氏合金C22以及超級奧氏體不銹鋼UNS N08367等合金的焊接，被廣泛應用于酰胺加熱器、煙氣脫硫系統、海水管道系統、酸洗系統以及復雜的制藥反應器的制造[1-4]。因此大量的管道焊接對焊條的焊接工藝性提出了較高的要求，同時工程應用環境對焊縫的耐腐蝕性及抗裂性能也提出了很高的要求[5]。

目前工程上大都采用進口焊材[6]。為了實現焊條的國產化，平、立焊工藝性的進一步改善，耐腐蝕性能的提高，抗裂性能的穩定都是目前國產ENiCrMo-10焊條需要解決的問題。

1 試驗要求與方法

1.1 技術要求

熔敷金屬主要化學成分及焊態力學性能的要求見表1、表2所示。側彎試樣彎曲180°后，受拉伸面上不允許出現超過3個長度在0.4 ～ 2.5 mm的裂紋。按照ASTM G48—2011《使用氯化鐵溶液測定不銹鋼和有關合金耐點腐蝕和縫隙腐蝕的標準試驗方法》標準中A法的要求進行試驗，要求表面無點腐蝕，且試樣平均腐蝕速率≤4 g/m2。按照ASTM G28—2002《鍛制高鎳鉻軸承合金晶間腐蝕敏感性的檢查用標準試驗方法》標準中A法的要求進行試驗，腐蝕速率≤12 mm/年。……