化學鍍Ni—W—P合金鍍層的耐蝕性研究

摘 要：通過正交實驗，以沉積速率和腐蝕速率為指標，獲得了優化化學鍍Ni-W-P鍍液配方。P和W的含量以及腐蝕介質的性質等因素有關，W對鍍層獲得非晶結構的作用要大于P的作用。

關鍵詞：化學鍍Ni-W-P合金 正交試驗 非晶 耐蝕性

中圖分類號： TQ134 文獻標識碼：A 文章編號：1674-098X（2014）05（b）-0026-03

Study on the Corrosion Resistance of Electroless Ni-W-P Alloy Coating

XU Zhen-yu，JIANG Shi-hang，LIU Yang-Da，CHU Yao

Mechanical Engineering，Yangzhou Univ，Yangzhou，225127，China

Abstract：Optimized process of electroless deposition of Ni-W-P alloy were determined by orthogonal experiment.Deposition rate and corrosion resistance were taken as the index for assessment.The anti-corrosion behavior of the Ni-W-P alloy coating was studied in the environment 10%H2SO4+30%HCl，and the results show that the corrosion resistance of Ni-W-P mainly depends on its amorphous structure， the content of P，W and the nature of the corrosive medium，the role of the W than the P in the aspect of amorphous structure.

Key words：electroless Ni-W-P orthogonal experiment Amorphous Corrosion Resistance

腐蝕是導致材料失效一個重要因素，給國民經濟帶來了巨大的損失。在很多領域，都對材料的耐蝕性能提出了很高的要求。化學鍍Ni-P合金鍍層在工業上已經獲得了廣泛的應用，在化學沉積Ni-P的基礎上，往化學鍍液中添加鎢酸鹽獲得的Ni-W-P鍍層則具有更加優良的耐蝕性能。但在對化學鍍Ni-W-P鍍液的工藝進行優化時，一般都以鍍層的沉積速度為指標，但沉積速率與耐蝕性并非一定成正比，因此考慮以鍍層沉積速率與耐蝕性相結合為共同評價指標，優化化學鍍Ni-W-P工藝參數，可以得到綜合性能優異的鍍層，同時對鍍層在H2SO4+HCl介質中的耐蝕機理進行研究，以期能進一步提高材料的耐蝕性能。

1 實驗

1.1 實驗過程

參考文獻

[1]王良洪，謝紅希，肖剛鋒.7075鋁合金化學鍍Ni-P/Ni-W-P雙層鍍層研究[J].表面技術，2012，41（2）：43-46.

[2]姚懷，萇清華，王喜然.鋁合金化學鍍Ni-W-P三元合金組織及性能的研究[J].表面技術，2010，39（3）：26-28.

[3]渠毓萍.鎂合金表面化學鍍Ni-P層的制備及其耐蝕性的研究[D].山西：太原理工大學，2005：61.

[4]于會生，姜秉元，李延祥.化學沉積Ni-P和Ni-W-P合金耐蝕性以及熱處理的影響[J].洛陽工學院學報，1997， 18（4）：15-18.

[5]喬學亮，許衛華.化學鍍Ni-P鍍層的組織和性能[J].金屬熱處理，1994（6）：26-27.

[6]謝躍勤，黃新民.化學鍍Ni-W-P三元合金工藝與性能研究[J].機械工人，2006（9）：26-28.