水性光油的研究

梁文波，鄭 軍，張士軍，劉 毅

（保定光普化工研究所，河北 保定 071000）

水性光油的研究

梁文波，鄭 軍，張士軍，劉 毅

（保定光普化工研究所，河北 保定 071000）

主要考察了Tg值、黏度調節樹脂H-8905、脫模劑H-862、耐磨蠟漿H-859對光油性能的影響。提出了滿足高光澤度和高耐磨性的上光光油和磨光光油配方。經上機驗證，上光油光澤度75以上，耐磨次數6000次以上；磨光油光澤度85以上，耐磨次數8000次以上，使用性能和VOC含量滿足出口要求。

水性光油；乳液聚合；光澤度；耐磨性；脫模劑；耐磨蠟漿

Abstract:The effects of Tg value,H-8905(viscosity adjusting resin),H-862(release agent)and H-859(wear resisting wax)on the performance of glazing oil were investigated.Depending on the result the glazing oil and buffing oil formulations were proposed which could meet the requirement of high glossiness and excellent wear resistance.According to the experimental data,the glossiness was above 75 and the wear resistance times was over 6000 of the glazing oil;and it was above 85 and over 8000 of the buffing oil.The performances and VOC content of products could meet the standard for export.

Key words:Waterborne glazing oil;emulsion polymerization;glossiness;wear resistance;release agent;wear resisting wax

引 言

光油是隨著包裝印刷業的快速發展而興起的一種產品。最初的紙質印刷包裝品直接暴露于環境中，易產生的弊端在于：材料易受潮，表面印刷的油墨層易磨損，包裝品基本無光澤或光澤度較低。針對這種情況，首先普遍采用的方式是對紙質印刷包裝品采用紙塑復膜的技術對其進行防護，能夠解決上述問題。紙塑復膜又帶來的一系列其他問題：廢包裝材料回收時，紙塑分離困難，分離成本加大，并直接導致大量廢棄物的產生，且某些出口包裝材料不允許采用復膜工藝。為降低分離成本，減少廢棄物的產生，通過采用對包裝材料進行涂層保護的辦法解決以上問題，即對印刷包裝品進行光油涂布，光油干燥成膜后形成防水、防潮、柔韌、耐磨且具有一定光澤的保護涂層，既滿足了印刷包裝品在美觀、實用等方面的要求，又避免了環境污染廢棄物的產生[1～4]。

針對環保性的要求，目前的光油以水性化的研究更具發展前景，溶劑型或醇基光油僅用在特殊的場合和時間段。……