水工混凝土干縮應(yīng)力分析和干縮試驗探討

王同生

(太湖流域管理局,上海 200434)

摘要:回顧了水工混凝土水分?jǐn)U散系數(shù)和干縮系數(shù)的非線性特性及其在徐變干縮應(yīng)力分析中的應(yīng)用,并對水工混凝土現(xiàn)行干縮試驗方法中存在的問題進行探討,指出按現(xiàn)行方法測定的干縮變形包含了自生體積變形,扣除后才能得到真正的干縮變形。對干縮變形實用計算法的適用條件和局限性進行了討論。

關(guān)鍵詞:水分?jǐn)U散;干縮應(yīng)力;干縮試驗;水工混凝土

中圖分類號:TV431文獻標(biāo)識碼:A文章編號:1006-7647(2010)06-0030-03

DOI:10.3880/j.issn.1006-7647.2010.06.008

作者簡介:王同生(1935—),男,江蘇泰縣人,教授級高級工程師,從事混凝土溫度和收縮應(yīng)力以及流域規(guī)劃和管理研究。E-mail:zhouhw999@sohu.com

Abstract:The nonlinear characteristics of moisture diffusion coefficient and shrinkage coefficient of hydraulic concrete and their application in creep shrinkage stress analyses were reviewed.The problems in the existing test methods for shrinkage of hydraulic concrete were discussed.It was put forward that the shrinkage deformation determined by the existing methods included the inherent volume deformation,and the actual shrinkage deformation was achieved by subtracting it.Finally,the applicable conditions and limitations of practical methods for shrinkage of hydraulic concrete were investigated.

Key words:moisture diffusion;shrinkage stress;shrinkage test;hydraulic concrete

混凝土在失去水分時就會收縮,這一過程稱為干縮。混凝土內(nèi)水分?jǐn)U散的速度很慢,大約是溫度傳導(dǎo)速度的1/1000。對于一面暴露于相對濕度為50%的空氣中的混凝土,干燥深度達到7 cm需要1個月,達到70cm則需要將近10年[1-2]。

干縮常常在混凝土表面引起細(xì)而淺的表面裂縫。達到一定寬度和深度的干縮裂縫會引起鋼筋混凝土結(jié)構(gòu)中鋼筋的銹蝕,在不利條件下會引起結(jié)構(gòu)的滲漏,影響結(jié)構(gòu)的耐久性。不同形式的結(jié)構(gòu)干縮裂縫的影響程度不相同。大體積混凝土不但尺寸大,且常常是無筋混凝土,受干縮裂縫影響小,基本上可以忽略;涵閘的底板和閘墩雖然平面尺寸也很大,但厚度較小,只有1～3m,為較大體積混凝土,且常常是配鋼筋的,受其一定的影響,需要加以注意;工業(yè)和民用建筑中的薄壁結(jié)構(gòu)采用鋼筋混凝土材料,且斷面尺寸很小,厚度只有幾十厘米,所受影響最大,更需要引起注意。……