低碳拉絲材用熱軋盤條SAE1008Cr質量分析及工藝改進

張秀香

摘 要：本鋼北營公司生產的低碳拉絲材用熱軋盤條SAE1008Cr，由于盤條折疊缺陷導致下游滾絲加工過程出現絲齒脫落和翹皮現象。通過鋼坯情況適當調整軋輥輥縫，防止因為軋輥調整不當而導致金屬在孔型中過盈充滿而從輥縫中溢出；正確安裝導衛，保證與孔型對中，防止因入口導衛偏斜、磨損嚴重，失去扶持作用。工藝優化后產品質量達到客戶要求。

關鍵詞：低碳拉絲材 折疊 工藝改進

中圖分類號：TG335.63 文獻標識碼：A 文章編號：1674-098X（2019）04（c）-0073-02

Abstract： BeiYing company of BX STEEL products the low carbon wire-drawing material SAE1008Cr，Due to the wire rod folded，it appears silk tooth loss and warp in the process of wire rolling . Adjusting roll seam on the basis of the billets condition.Prevent the phenomenon from happening. Which is if the metal that is full in the roll seam can spill，because of the roll seam is misalignment.Install the guide accurately，Assure that the guide and the roll seam is in a line.Prevent the guide against losing the supporting role because of the guide is slant or worn。By the process improvement，the product quality meets customer requirements.

Key Words： Low carbon wire-drawing material； Wire rod folded； Process improvement

本溪北營公司生產的出口韓國低碳拉絲材用熱軋盤條在滾絲加工過程出現絲齒脫落、翹皮現象，對樣品取樣分析，具體情況如下。

1 樣品宏觀形貌

低碳拉絲材用熱軋盤條SAE1008Cr在滾絲加工過程出現絲齒脫落、翹皮現象，并出現在螺絲桿同一側位置。同時對母材盤條樣品觀察，可以發現盤條表面存在明顯的通條折疊缺陷。詳見圖1和圖2。

2 檢驗分析

2.1 化學檢驗分析

如表1所示。

試樣實際檢測成分滿足標準和放行要求。

2.2 顯微組織檢驗

對問題樣品進行顯微組織檢驗，詳見圖3和圖4。

通過對母材樣品進行金相顯微觀測，可以看到通條裂痕缺陷位置在靠近表面處存在呈一定角度的壓入性裂紋缺陷，裂紋的兩側沒有脫碳現象，并且靠近裂紋根部呈圓頓狀態。

樣品的非金屬夾雜物除均在1.0級別以下。

結合宏觀樣品缺陷特征判斷，該缺陷為折疊壓入導致在滾絲加工過程出現了絲齒脫落、翹皮。

3 盤條折疊產生原因及控制措施

3.1 盤條折疊產生原因

金屬在孔型中過盈充滿而從輥縫中溢出或導衛偏斜、磨損嚴重，軋件在孔型中不穩定而傾斜倒鋼，產生耳子。

3.2 控制措施

（1）軋鋼廠根據煉鋼來料情況適當調整軋輥輥縫，防止因為軋輥調整不當而導致金屬在孔型中過盈充滿而從輥縫中溢出。

（2）正確安裝導衛，保證與孔型對中，并勤檢查入口導板磨損情況，防止因入口導衛偏斜、磨損嚴重，失去扶持作用，軋件在孔型中不穩定而傾斜倒鋼，產生耳子，在下一孔型中形成折疊。

4 結語

低碳拉絲材用熱軋盤條因折疊壓入導致在滾絲加工過程出現了絲齒脫落、翹皮缺陷。根據鋼坯來料情況適當調整軋輥輥縫，防止因為軋輥調整不當而導致金屬在孔型中過盈充滿而從輥縫中溢出；此外，通過正確安裝導衛，保證與孔型對中，并勤檢查入口導板磨損情況，防止因入口導衛偏斜、磨損嚴重，失去扶持作用等措施控制折疊的產生。